Typical Mechanical Properties for Direct Metal Laser Sintering (DMLS & SLM) Components
| Alloy Material | Tensile Strength (Rm) | Yield Strength (Rp0.2) | Elongation at Break | Primary Applications |
|---|---|---|---|---|
| AlSi10Mg (Aluminum) | 400 ± 20 MPa | 240 ± 15 MPa | 6 - 8 % | Lightweight aerospace brackets, EV heat sinks, motorsport housings |
| Ti6Al4V (Titanium Grade 5) | 1,250 ± 50 MPa | 1,100 ± 50 MPa | 10 - 12 % | High-stress structural components, turbine blades, medical implants |
| Inconel 718 (Nickel Alloy) | 1,350 ± 60 MPa | 1,150 ± 50 MPa | 12 - 15 % | High-temperature rocket engine parts, exhaust manifolds, tooling inserts |
| Maraging Steel 300 (1.2709) | 2,000 ± 80 MPa | 1,900 ± 70 MPa | 3 - 5 % | Conformal cooled injection molds, high-load industrial tooling |
| Stainless Steel 316L (1.4404) | 640 ± 30 MPa | 530 ± 25 MPa | 35 - 40 % | Corrosion-resistant manifolds, food processing equipment, chemical impellers |